③原料技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 物理性能 | 比重 | ASTM D-792 | 1.1 | |||
| 阻燃性 | UL 94 | 1.6 | mm | |||
| 阻燃性 | UL 94 | HB | ||||
| 模具收缩率 | 3.2mm | ASTM D-955 | 11-13 | 10-3 | ||
| 机械性能 | 弯曲强度 | 6.4mm | ASTM D-790 | 96 | MPa | |
| 弯曲模量 | 6.4mm | ASTM D-790 | 2246 | MPa | ||
| 洛氏硬度 | ASTM D-785 | 116 | ||||
| 缺口冲击强度 | 23°C | ASTM D-256 | 240 | J/M | ||
| 拉伸强度 | 屈伏点 | 3.2mm | ASTM D-638 | 59 | MPa | |
| 断裂点 | 3.2mm | ASTM D-638 | 60 | MPa | ||
| 热性能 | UL长期使用温度 | 电气 | UL 746B | 50 | °C | |
| 含冲击 | UL 746B | 50 | °C | |||
| 无冲击 | UL 746B | 50 | °C | |||
| 线膨胀系数 | ASTM E-831 | 9.0×10-5 | 1/°C | |||
| 热变形强度 | 0.45MPa | ASTM D-648 | 193 | °C | ||
| 热变形温度 | 1.8MPa | ASTM D-648 | 143 | °C | ||
| 维卡软化点 | ASTM D-1525 | 232 | °C | |||